Forum Index > Off-topic Talk > straight lines in pattern welded blades? Reply to topic
This is a standard topic  
Author Message
Carl W.




Location: usa
Joined: 07 Aug 2008

Posts: 182

PostPosted: Sat 04 Dec, 2010 1:48 pm    Post subject: straight lines in pattern welded blades?         Reply with quote

I have done some searching but its still not obvious to me why there often (if not always) are really straight looking boundaries between twisted bars, & also between twisted bars & edge steel. I would have assumed (knowing very little) that the welding process was pretty messy, & so would not look so straight & neat. I am mainly referring to modern reproductions, where it shows so clearly.

Is it simply that the bars are ground flat after twisting, prior to welding, or...?

Sorry for the (likely very) dumb question. Thanks!
View user's profile Send private message
Luka Borscak




Location: Croatia
Joined: 11 Jun 2007
Likes: 7 pages

Posts: 2,307

PostPosted: Sat 04 Dec, 2010 1:54 pm    Post subject:         Reply with quote

Have you seen a series of pictures at the bottom of the Armart page with their pattern welded swords? It helps in imagining how the process goes...
http://www.armart.antiquanova.com/Viking_pattern_welded.htm
View user's profile Send private message
R D Moore




Location: Portland Oregon
Joined: 09 Jun 2007
Likes: 7 pages
Reading list: 11 books

Spotlight topics: 1
Posts: 425

PostPosted: Sat 04 Dec, 2010 2:02 pm    Post subject:         Reply with quote

Here's a link to a WIP by a French bladesmith that should answer your question:
http://forums.dfoggknives.com/index.php?showtopic=14400

"No man is entitled to the blessings of freedom unless he be vigilant in its preservation" ...Gen. Douglas Macarthur
View user's profile Send private message Send e-mail
Bernard Delor




Location: France
Joined: 19 Nov 2010

Posts: 51

PostPosted: Sun 05 Dec, 2010 3:23 am    Post subject:         Reply with quote

Hello,

yes you are right, the bars are ground flat after twisting, prior to welding. Moreover, sometimes a thin layer of plain steel in inserted between each bar, in order to make thicker and more visible boundaries.
There is no need to provide a lot of strength in the welding process of the bars. When doing it carefully, the welding lines can remain quite straight.
To show you how the forging may keep the inside pattern "safe", here is a blade made by widthwise forging of a simple layered bar. You can see that all the layers remain pretty straight.



 Attachment: 36.65 KB
2008-10-ChasseDamasSurChant-taille600-1.jpg

View user's profile Send private message Visit poster's website
Chad Arnow
myArmoury Team


myArmoury Team

PostPosted: Sun 05 Dec, 2010 6:14 am    Post subject:         Reply with quote

Think of it this way: straight lines are just one pattern that can be put into pattern welding and they're the foundation of pattern welding. You're seeing the layers that go into pattern welding and they haven't been twisted/manipulated into some other pattern.
Happy

ChadA

http://chadarnow.com/
View user's profile Send private message Send e-mail Visit poster's website
Luka Borscak




Location: Croatia
Joined: 11 Jun 2007
Likes: 7 pages

Posts: 2,307

PostPosted: Sun 05 Dec, 2010 8:28 am    Post subject:         Reply with quote

I think Carl talks about lines between different rods in the pattern welded core, for example three rods visible in the core of a Hanwei Saxon, not lines between the layers.
View user's profile Send private message
Carl W.




Location: usa
Joined: 07 Aug 2008

Posts: 182

PostPosted: Sun 05 Dec, 2010 9:41 am    Post subject:         Reply with quote

Luka is correct about my question, & shows a good example. Here is another, & there are many more, where the lines look really, really, (really!) straight.

http://www.templ.net/pics-weapons/104-sword/1...lade-v.jpg

However, the closeups shown in below (got there by way of RD's interesting D.Fogg link), especially the 2nd pic down, show that the lines are not always so straight, & wander around some. This is more what I would have expected to be typical, figuring the welding process is messy.

http://www.elfic.fr/anglais/pages/viking-sword.htm

Bernard Delor wrote:

yes you are right, the bars are ground flat after twisting, prior to welding. Moreover, sometimes a thin layer of plain steel in inserted between each bar, in order to make thicker and more visible boundaries.


So far (I think) I learned that the really really straight cases were ground very flat after twisting, prior to welding. I'd guess the less straight, wandering, & more random cases were not ground so much (correct me if I'm wrong). Does the latter wandering case make the welding work much more tricky?
View user's profile Send private message
Peter Johnsson
Industry Professional



Location: Storvreta, Sweden
Joined: 27 Aug 2003
Reading list: 1 book

Spotlight topics: 3
Posts: 1,757

PostPosted: Sun 05 Dec, 2010 10:08 am    Post subject:         Reply with quote

How straight the weld lines between rods/billets are in the finished blade depends a lot on how they are forged. Some styles are often anything but straight, while other demand pretty straight lines.

Twisted bars can be forged square to pretty tight tolerances, or (and) ground flat (and clean) prior to final welding. This can have an impact on final straightness, but so will also amount and type of forging of the final billet after final welding. A lot of shaping and manipulation of width/thickness & shape can cause process of forging leaving undulating lines. Not always, but sometimes.
You do not always want/need a lot of forging after the billet/blank is welded for the last time. It depends (again).

Twisted bars can also be welded together to a blade blank without prior square forging and/or grinding. Then you will see some slight undulating lines between the rods. Sometimes. Depends on how much the billet is ground to reveal the pattern.

I will not pretend to be an expert on pattern welding. But this is according to my own (rather limited) experience and from seeing the work of others, both contemporary and ancient smiths.

Straight lines can be a proof of good hammer control and/or careful cleaning/grinding of the billets. To get straight lines you have to forge evenly and carefully. It takes a bit of hammer control and the ability to keep the work square and even through out the process.

Sometimes you do want a bit of organic undulation and irregular thickness of the layers as this is a very common thing to see on originals. Not all, but some and it can be a very characteristic feature.
View user's profile Send private message Visit poster's website
Glen A Cleeton




Location: Nipmuc USA
Joined: 21 Aug 2003

Posts: 1,968

PostPosted: Sun 05 Dec, 2010 10:52 am    Post subject:         Reply with quote

Confessions of a bladesmith; secrets revealed!
Kevin R. Cashen

http://forums.swordforum.com/showthread.php?t=13809


Kevin walks through the making of one of these twisted and edge welded examples.

Cheers

GC
View user's profile Send private message


Display posts from previous:   
Forum Index > Off-topic Talk > straight lines in pattern welded blades?
Page 1 of 1 Reply to topic
All times are GMT - 8 Hours

View previous topic :: View next topic
Jump to:  
You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot vote in polls in this forum
You cannot attach files in this forum
You can download files in this forum






All contents © Copyright 2003-2024 myArmoury.com — All rights reserved
Discussion forums powered by phpBB © The phpBB Group
Switch to the Basic Low-bandwidth Version of the forum